intonga yegraphite ecocekileyo ephezulu
Hebei Hexi Carbon Co., LTD.Ucoceko oluphezulu lwegraphite intonga yemveliso ebonakalayo kunye nekhemikhali yesalathiso setafile.
Izithuthi zamandla amatsha, ukuphosa okuqhubekayo kunye namanye amashishini asetyenziswa ekusebenzeni kwemathiriyeli yegraphite | ||||||||||
Uphawu | Ukuxinana | Ukumelana nombane | Ukuqhuba kobushushu | I-Coefficient yokwandiswa kwe-thermal (ubushushu begumbi -600 ℃) | Ukuqina konxweme | Amandla e-Flexural | Amandla acinezelayo | Imodyuli ye-elasticity | uthuthu | Umxholo wothuthu ococekileyo |
g/cm3 | µΩm | W/mk | 10-6/℃ | HSD | Mpa | Mpa | I-Gpa | PPM | PPM | |
HX-5 | 1.80 | 8~10 | 125 | 4.9 | 45 | 40 | 80 | 9.5 | 500 | 50 |
Iinkcukacha zokusebenza zezixhobo zegraphite ezicinezelekileyo ze-isostatic zokuphosa ubushushu obuphezulu kunye ne-hydrogen fuel cell bipolar plate industry | ||||||||||
Uphawu | Ukuxinana | Ukumelana nombane | Ukuqhuba kobushushu | I-Coefficient yokwandiswa kwe-thermal (ubushushu begumbi -600 ℃) | Ukuqina konxweme | Amandla e-Flexural | Amandla acinezelayo | Imodyuli ye-elasticity | uthuthu | Umxholo wothuthu ococekileyo |
g/cm3 | µΩm | W/mk | 10-6/℃ | HSD | Mpa | Mpa | I-Gpa | PPM | PPM | |
HX-5P | 1.90 | 8~10 | 135 | 3.6 | 55 | 55 | 105 | 12 | 500 | 50 |
Isalathiso sokusebenza sezixhobo zegraphite ezicinezelweyo ze-isostatic kwishishini le-photovoltaic | ||||||||||
Uphawu | Ukuxinana | Ukumelana nombane | Ukuqhuba kobushushu | I-Coefficient yokwandiswa kwe-thermal (ubushushu begumbi -600 ℃) | Ukuqina konxweme | Amandla e-Flexural | Amandla acinezelayo | Imodyuli ye-elasticity | uthuthu | Umxholo wothuthu ococekileyo |
g/cm3 | µΩm | W/mk | 10-6/℃ | HSD | Mpa | Mpa | I-Gpa | PPM | PPM | |
HX-4 | 1.72 | 10–13 | 100 | 5 | 40 | 30 | 65 | 9.2 | 500 | 50 |
HX-6 | 1.81 | 11-14 | 120 | 4.5 | 60 | 45 | 90 | 10.5 | 500 | 50 |
Iipropathi zezinto zegraphite ezicinezelweyo ze-isostatic ezisetyenziswa kwishishini le-EDM | ||||||||||
Uphawu | Ukuxinana | Ukumelana nombane | Ukuqina konxweme | Ubunzima beRockwell | Amandla e-Flexural | Umndilili wobungakanani beenkozo | ||||
g/cm3 | µΩm | HSD | HRL | Mpa | μm | |||||
I-KYX-7 | 1.76 | 12-16 | 40 | 94 | 40 | 8 | ||||
I-KYX-60 | 1.78 | 12-16 | 45 | 100 | 45 | 4 | ||||
I-KYD-8 | 1.84 | 12-16 | 70 | 105 | 55 | 6 |
Iglasi yokugoba eshushu ye-3D kunye namanye amashishini anezalathi zokusebenza ze-isostatic ezicinezelekileyo zegraphite | |||||||||
Uphawu | Ukuxinana | Ukumelana nombane | Ukuqhuba kobushushu | I-Coefficient yokwandiswa kwe-thermal (ubushushu begumbi -600 ℃) | Ukuqina konxweme | Amandla e-Flexural | Amandla acinezelayo | Imodyuli ye-elasticity | Umndilili wobungakanani beenkozo |
g/cm3 | µΩm | W/mk | 10-6/℃ | HSD | Mpa | Mpa | I-Gpa | μm | |
I-KYD-9 | 1.88-1.92 | 10–14 | 110 | 3.9 | 75 | 60 | 125 | 12 | 2 |
I-KYD-30 | 1.81 | 15–19 | 80 | 5.8 | 80 | 43 | 130 | 7.5 | 12 |
KYX-700 | 1.85 | 12-16 | 105 | 4 | 55 | 50 | 105 | 10 | 8 |
I-KYX-60S | 1.85 | 12-16 | 110 | 4 | 60 | 55 | 120 | 11 | 4 |